Special Steel/Steel Plate/Steel Sheet/Steel Bar/Alloy Steel/Mould Steel H11 (1.2343)
Oct 27, 2017

Basic Info

  • Model NO.: H11

  • Standard: AISI, ASTM, DIN

  • Technique: Hot Forged or Hot Rolled

  • Surface Treatment: Black Surface, Grinded,Peeled,Milled,Polished

  • Application: Die Steel Bar

  • Smelting Process: Ef, Eaf, ESR

  • Surface Condition: Black Surface, Grinded,Peeled,Milled,Polished

  • Transport Package: Seaworth Packing

  • Origin: Huangshi, Hubei

  • Type: Flat

  • Composition: Ferrous Steel Scrap

  • Shape: Round,Flat or Square

  • Special Use: Mold Steel

  • Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm

  • Delivery Condition: Hot Rolled, Forged, Annealed,Quenched and Tempered

  • Trademark: KAIXIN

  • Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm

  • HS Code: 7228100000

Product Description

Introduction:

Chromium hot work tool steels are designated as group H steels according to the AISI classification system. This series of steels start from H1 to H19. The most commonly used chromium hot work steels are H11, H12, and H13, which can be air hardened in 150 mm thick sections. The steels are subjected to minimal distortion during hardening due to their balanced alloy content. The tools produced from chromium hot work steels can be cooled using water without damage as these steels have low carbon and alloy contents.
This article will give an overview of H11 chromium hot work steels, which have low carbon content and good toughness. These hot work steels can be deep hardened by heat treatment and air-quenching.

Applications:

H11 Hot Work Steels is often used for highly stressed structural parts such as aircraft landing gear. It resists softening at temperatures up to 1000 F while retaining good ductility and toughness even at strength levels on the order of 275 ksi.
Quality Standard: 
ASTM A681 Standard Specification for Tool Steel
All Grades Comparison:

ASTMAFNORDINUNIJISB.S.
H11Z 38 CDV 51.2343T20811SKD6BH 11

Chemical Composition(%):

CSiMnPSCrVMo
0.33-0.430.80-1.250.20-0.600.030 max0.030 max4.75-5.500.30-0.601.10-1.60

HEAT TREATMENT:
FORGING: H11 hot work steels are forged at 1121°C (2050°F). For this type of steels, forging below 899°C (1650°F) is not preferable.
ANNEALING: H11 hot work steels are annealed at 871°C (1600°F) and slowly cooled at 4°C (40°F) in the furnace.
HARDENING: Preheat to 1500 °F and then heat to 1850 °F and hold for 15 to 40 minutes. Air cool (air quench).
TEMPERING: Tempering is carried out on H11 tool steels at temperature ranging from 538 to 649°C (1000 to 1200°F) to obtain Rockwell C hardness of 54 to 38. Double tempering can also be performed in these steels every one hour at the preferred tempering temperature.
Mechanical Properties:

PropertiesMetricImperial
Hardness, Rockwell C (air cooled from 982°C, 45 mins)52.552.5
Hardness, Rockwell C (air cooled from 1010°C, 45 mins)5656
Hardness, Rockwell C (air cooled from 1038°C, 45 mins)5757
Modulus of elasticity207 GPa30000 ksi
Modulus of elasticity (@538°C/1000°F)159 GPa23000 ksi
Modulus of elasticity (@204°C/400°F)190 GPa27500 ksi
Charpy impact (V-notch; air cooled from 1010°C;535°C temper temperature)13.6 J10.0 ft-lb
Charpy impact (V-notch; air cooled from 1010°C;650°C temper temperature)27.1 J20.0 ft-lb
Charpy impact (V-notch; air cooled from 1010°C;370°C temper temperature)33.9 J25.0 ft-lb
Machinability (1% carbon steel)75.0 - 80.0%75.0 - 80.0%
Poisson's ratio0.27-0.300.27-0.30

Hubei Kaixin Supply Chain Management Co., Ltd.

TEL +8618272169977 ; 0714-6510168

FAX0714-6519746

Emailinfo@hubeikaixin.com

AddNo.37 Huahu Ave Huahu Street.Huangshi City Hubei

Code435000

web:www.kxdiesteel.com