Hot Forged Mould Steel Module H13
Sep 18, 2017

Basic Info

  • Model NO.: H13

  • Standard: AISI, ASTM, DIN, GB

  • Technique: Forged

  • Surface Treatment: Power Cocating

  • Application: Die Steel Bar

  • Transport Package: Customized

  • Origin: hubei, China

  • Type: Square

  • Composition: Stainless Steel Scrap

  • Shape: Round or Plate

  • Special Use: Mold Steel

  • Trademark: KAIXIN

  • Specification: 2T-55T size and material are customized

Product Description

Product Description
Tool Steel Plate/Steel Sheet,SKD11, SKD61, 1.2379, 1.2344, 1.2510, 1.2311, 

1.2312, 1.2083, 1.2316 Mould Steel/ Special Steel/Alloy Steel

> It widely used in hot work and cold work tooling applications. 
> It resists thermal fatigue cracking which occurs as a result of cyclic 

heating and cooling cycles in hot work tooling applications. 
> Its excellent combination of high toughness and resistance to thermal 

fatigue cracking (also known as heat checking) H13 is used for more hot 

work tooling applications than any other tool steel. 
> With good stability in heat treatment, H13 is also used in a variety of cold work tooling applications. In these applications, H13 provides better 

hardenability (through hardening in large section thicknesses) and better wear 

resistance than common alloy steels. 
> Also available as Electro-Slag-Remelted (ESR) products as well. 

The remelting processes provide improved chemical homogeneity, refinement of carbide size. 

Heat Treatment: 
Forge: At 1050° C-1095° C Cool slowly and anneal then. 
Annealing: At 843° C-898° C; Cool slowly in furnace 
Stress Relieving: Heat slowly to 566° C-676° C, and then cool in still air. 
Hardening: Preheat to 815° C and then heat to 1010° C and hold for 15 to 40 minutes. 

Air cool (air quench) 

APPLICATIONS: Inserts, cores, and cavities for die casting dies, 

die casting shot sleeves, hot forging dies, extrusion dies, 

and plastic mold cavities and components that require high toughness 

and excellent polishability. 

Chemical Composition(%): 
C:  0.32-0.45 
Si:  0.80-1.20 
Mn:  0.20-0.50 
P:  max. 0.025 
S:  max. 0.025 
Cr:  4.75-5.50 
Mo:  1.10-1.75 
V:  0.80-1.20 
Cu:  max. 0.030 

Common Size: Round bars: Dia. 80-600mm Plates: Thickness: 40-350mm Width: 100-1000mm, 

Length: 2m-6m. 

Delivery condition: EAF+LF+VD+(ESR), forged, anealed, UT tested, peeled or machined. 

Hardness HBW: < =235HB 

Tolerance: 0/+2mm 

Forging Ratio: Min 1: 4 

Surface: Rounds: Black / grinded / turned Plates: Black / milled 

Surface condition: Cracks, decarburisation, 

burd spots and similar surface defects just within permissible tolerances. 

Grain size: ASTM E112 5-8 

Inclusion rating: 
According to ASTM E45 

TYPE   A   B   C   D 
THIN  0.5-2.0  0.5-2.0  0.5-2.0  0.5-2.0 
THICK  0.5-2.0  0.5-2.0  0.5-2.0  0.5-2.0 
Or K4 max. 30 according to DIN 50602 

UT Grade: Sep 1921-84 Group 3 Class D/d Qualified. 

Delivery time: According to your needs to discuss

Quality assurance: ISO9001: 2008, IQNet, CQC

Hubei Kaixin Supply Chain Management Co., Ltd.

TEL +8618272169977 ; 0714-6510168



AddNo.37 Huahu Ave Huahu Street.Huangshi City Hubei