1.2581 Hot Work Tool Steel
Oct 16, 2017

Basic Info

Product Description

  • Model NO.: 1.2581

  • Standard: AISI, ASTM, DIN, JIS, GB, BS

  • Technique: Forged

  • Surface Treatment: Color Coated; Polished

  • Application: Die Steel Bar

  • Type: Carbon Steel Bar

  • Composition: Ferrous Steel Scrap

  • Shape: Round; Plat

  • Special Use: High-strength Steel Plate, Wear Resistant Steel, Silicon Steel, Cold Heading Steel, Free Cutting Steel, Mold Steel

  • Specification: Dimensions: 15-300mm

Hot work tool steel H21/SKD5/1.2581
Steel grade:   AISI H21, JIS SKD5, DIN 1.2581, GB 3Cr2W8V
Size: 

 

round barsdiameter(mm)length(mm) -
 50~500 2000~5800 -
flat steelthichkness(mm)width(mm)length(mm)
20~40080~10002000~5800

Chemical composition(for reference only):

CSiMnCrWvPS
0.30~0.400.40 MAX0.40 MAX2.20~2.707.50-9.000.20-0.50≤0.030≤0.030


Soft Annealing: Heat to 780-810°C, cool slowly. This will produce a maximum Brinell   hardness of 240.  
Stress Relieving: Stress relieving to remove machining stresses should be carried out by heating to 650°C, holding for one hour at heat, followed by air cooling. This operation is performed to reduce distortion during heat treatment.
Hardening: Harden from a temperature of 1080-1160°C followed by air, oil or warm bath quenching. Hardness after quenching is 47-53 HRC.  
Tempering 
Tempering temperature: See the table bellow. 
Tempering Temperature (oC) vs. Hardness (HRC)


400°C     500°C     550°C       600°C       650°C    700°C
  
 49        49         51          50        46          36

Charateristics:  
   a. SKD5 Alloy steel is a hot work tool steel with dry hardening,have upper hot intensity and rigidity, under middle  pemperature,
   b. 1.2581 mould steel have good tenacity
   c. Hot tirdness nature and definite wearable empty quench under lower Ao shi ti temperature condition, small    distortion after heat treatment and so on.
Delivered Condition:    hot rolled and forged, annealed, black(ground or peeled )surface
Terms of Payment:  T/T, L/C,
Application:  Die Steel  H21/SKD5/1.2581   is for making punch and die under high temperature and stress without shock load,high temperature thermal cut pieces
Suitable for making of aluminum, zinc and copper alloy extrusion dies, casting dies and hot shearing blades, etc
Small silver polish steel (scaled and cold drawn), which is an ideal material for ejection pins and sleeves.
Also suitable for manufacture of plastic molds of high productiveity and long service life.


Hubei Kaixin Supply Chain Management Co., Ltd.

TEL +8618272169977 ; 0714-6510168

FAX0714-6519746

Emailinfo@hubeikaixin.com

AddNo.37 Huahu Ave Huahu Street.Huangshi City Hubei

Code435000

web:www.kxdiesteel.com