Good Price O1 Cold Work Rolled Tool Steel With Good Quality

Good Price O1 Cold Work Rolled Tool Steel With Good Quality
good price O1 cold work rolled tool steel with good quality Quick Details Steel Grade: 1.2510, 100MnCrW4, O1 Standard: AISI, ASTM, BS, DIN, GB, JIS Dimensions: Dia 2mm~1500mm Place of Origin: Hubei, China (Mainland) Brand Name: KAIXIN Model Number: 1.2510/ 100MnCrW4/ O1 Technique: Hot rolled /...
Chat Now

Product Details

good price O1 cold work rolled tool steel with good quality

Quick Details

Steel Grade: 1.2510, 100MnCrW4, O1

Standard: AISI, ASTM, BS, DIN, GB, JIS

Dimensions: Dia 2mm~1500mm

Place of Origin: Hubei, China (Mainland)

Brand Name: KAIXIN

Model Number: 1.2510/ 100MnCrW4/ O1

Technique: Hot rolled / Cold draw / Forged

Application: Cold work tool steel

Alloy Or Not: Is Alloy

Special Use: Mold Steel

Type: Alloy Steel Bar

Surface Treatment: black/polished/machined/peeled/grinded/turned

Length: 500mm~5800mm

Warranty: MTC / 3.1B

Shape: round bar / plate / flat / sheet

Certification: ISO9001, SGS, REACH, API

Delivery condition: Hot rolled or forged, Peeled or black surface, annealed or QT.

Testing: UT, Mechanics, Physical testing, Elements analysis

General Information:

With chromium-manganese content possessed good machinability, mechanical wear resistance and edge holding quality. Vanadium-Wolfram content reduces high working temperature wear and retention of temper temperature.  

Comparable standards:               

AISI/SAE

DIN

W.Nr.

Assab

JIS

BS

SIAU

GB,YB

O1

100MnCrW4

1.2510

DF2

SKS3

D3

K12

MnCrWV

Chemical composition: 

C

Mn

Si

Cr

V

W

P

S

0.90-1.05

1.00-1.20

0.15-0.35

0.50-0.70

0.05-0.15

0.50-0.70

≤0.03

≤0.03

Heat treatment

Hardening:

-  Temperature: 780-830°C(Slow heating and pre-heat at 350°Cand 650°C).

-  Duration: 30 mins per 25mm thick.

Quenching:

-  Medium: warn oil, salt bath.

Double Tempering

-  Temperature (2 hrs minimum) 250°C, better toughness.(58-59HRC).

-  Temperature (2 hrs minimum) 200°C, higher hardness. (60-61HRC).

Hubei Kaixin Supply Chain Management Co., Ltd.

TEL +8618272169977 ; 0714-6510168

FAX0714-6519746

Emailinfo@hubeikaixin.com

AddNo.37 Huahu Ave Huahu Street.Huangshi City Hubei

Code435000

web:www.kxdiesteel.com 


Hot Tags: good price o1 cold work rolled tool steel with good quality, China, suppliers, wholesale, customized
Related Products

Feedback