S1 Alloy Tool Steel, Cold Work Die SteelS1 Alloy Tool Steel,Cold Work Die Steel
Sep 14, 2017

Basic Info

  • Model NO.: S1

  • Standard: AISI, ASTM, DIN, JIS, GB, BS

  • Technique: Forged

  • Surface Treatment: Machined,Black Surface,Grined,Peeled

  • Application: Tool Steel Bar

  • Transport Package: Nude Packing

  • Origin: Huangshi, Hubei

  • Type: Alloy Steel Bar

  • Composition: Alloy Steel Scrap

  • Shape: Bar

  • Special Use: Wear Resistant Steel, Mold Steel

  • Trademark: KAIXIN

  • Specification: R: dia60-610mm; F20-300X100-610mm

  • HS Code: 7228400000

Product Description

S1 Alloy Tool Steel,Cold Work Die Steel

S1









Chemical
Composition
CSiMnCrPSMoVW
0.40-0.550.15-1.200.10-0.401.00-1.800.03MAX0.03MAX0.50 MAX0.15-0.30
1.50-3.00
Available
size
Round BarDiameterLength
16-800mm2000-6000mm
Flat BarThicknessWidthLength
16-400mm100-800mm2000-6000mm
Surface
condition
Black surface/ Grinded/ Machined
Annealed
hardness
HB212MAX
CharacteristicsAISI S1 is a versatile chrome-tungsten shock-resisting tool steel. Its properties provide excellent service in both cold and hot work shock applications. In addition, it is widely used for master hobs.
It's low carbon content provides toughness and its combination of alloying elements provides the carbide formation necessary for abrasion resistance, the hardenability necessary for shock tools, and improved hot work characteristics.
For additional wear resistance, tools of SI may be carburized during pack hardening.
ApplicationsHeavy duty blanking and forming dies, punches, chisels, shear blades, slitter knives, cold
striking dies, cold extrusion tools, coining dies, master hobs.
Hot work applications with operating temperatures under 1050F such as headers, piercers, forming tools, shear blades, and drop forge die inserts.
Heat
Treatment
S1 can be softened to proper structure for machining by heating slowly to 1450 to 1500°F, holding at temperature for at least one hour per inch of greatest thickness, and cooling slowly to 1000°F, after which it may be air- cooled. Hardness resulting from this treatment will be Brinell 212 max. To prevent decarburization, pack or pipe-anneal in sealed containers, using inert material or use a controlled atmosphere furnace.

Hubei Kaixin Supply Chain Management Co., Ltd.

TEL +8618272169977 ; 0714-6510168

FAX0714-6519746

Emailinfo@hubeikaixin.com

AddNo.37 Huahu Ave Huahu Street.Huangshi City Hubei

Code435000

web:www.kxdiesteel.com