DIN1.2312 P20+S Plastic Mold Steel
Sep 18, 2017

Basic Info

  • Model NO.: DIN1.2312 P20+S

  • Standard: AISI, ASTM, DIN

  • Technique: Hot Forged,or Hot Rolled

  • Surface Treatment: Black Surface, Grinded,Peeled,Milled,Polished

  • Application: Die Steel Bar

  • Smelting Process: Ef, Eaf, ESR

  • Surface Condition: Black Surface, Grinded,Peeled,Milled,Polished

  • Specification: Round Bar: Dia12~420mm Flat Bar: 2~420 X 30~1500mm

  • HS Code: 7228100000

  • Type: Round

  • Composition: Ferrous Steel Scrap

  • Shape: Round,Flat or Square

  • Special Use: Mold Steel

  • Size Range: Round Bar:Dia12~420mm Flat Bar:2~420 X 30~1500mm

  • Delivery Condition: Hot Rolled, Forged, Annealed,Quenched and Tempered

  • Trademark:KAIXIN

  • Origin: Huangshi, Hubei

Product Description


Introduction
P20+S Plastic mold steel with excellent machinability properties because 

of the high Scontent, good toughness properties, good wear resistance, 

uniform hardness in all dimensions, dimensional stability, 

requiring no heat treatment, 280-325HB hardened and tempered condition, suitable for nitriding to 

increase wear resistance, not suitable for chrome plating, polishing 

and etch graining.

Applications
P20+S Plastic Mold Steel is ideally suited for the production of moulds 

where improved machinability is required. Typical applications include die holders, 

zinc die casting dies, backers, bolsters and injection moulds. 

The versatility of this plastic mould tool steel with its 

high tensile characteristics enables uses for a variety of other 

applications such as shafts and wear strips.

Quality Standard

ASTM A681Werkstoff
P20+S1.2312


Chemical Composition(%)

CSiMnPSCrMo
0.35-0.450.30-0.501.40-1.600.030max0.05-0.101.80-2.000.15-0.25

HEAT TREATMENT
Forging: Heat slowly, allowing sufficient time for the steel 

to become heated through. Begin forging at 1050°C. 

Do not forge below 930°C reheating if necessary. 

After forging, cool very slowly.
Annealing: Heat uniformly to 710-740°C. Soak well, 

cool slowly in the furnace.
Stress Relieving:When dies are heavily machined, 

we recommend stabilising just before finish machining in order to relieve 

machining strains. 

Heat to 460-500°C. Soak well and allow to cool in the air.
Hardening: Heat uniformly to 830-870°C until heated through. Quench in oil.
Tempering: Heat uniformly and soak at the tempering temperature for 

at least one hour per 25mm of section. Allow to cool in still air.

Tempering TemperatureHardness(HRC)Tensile Strength (Mpa)
100oC511730
200oC501670
300oC481570
400oC461480
500oC421330
600oC361140

Nitriding: Tools machined from pre-hardened P20+S Plastic Mold Steel may be nitrided to give a 

wear resistant case of approximately Rockwell C60 surface hardness 

with a case depth of 0.35mm to 0.5mm. 

Nitriding also increases the corrosion resistance. After nitriding at 525°C 

in ammonia gas the surface hardness of the tool will be approximately 650HV.

TemperatureTime (hours)Approx. Depth of Case (mm)
525oC200.3
525oC400.35
525oC600.50

Case Hardening: Tools produced from P20+S Plastic Mold Steel 

may be case hardened, 

which can achieve a surface hardness of between 55 to 59 Rockwell C.
Hard Chromium Plating: To avoid hydrogen embrittlement P20+S Plastic 

Mold Steel should be tempered for 4 hours at 180°C for 4 

hours after hard chromium plating
Induction Hardening:Induction or flame hardening of will achieve 

a hardness of 50 to 55HRc. It is preferable to air cool, 

though smaller components may 

require forced cooling. Temper immediately after hardening.

Mill′s test certificate
EN 10204/3.1 with all relevant data reg. chem. composition, mech. 

properties and results of testing.
 

Hubei Kaixin Supply Chain Management Co., Ltd.

TEL +8618272169977 ; 0714-6510168

FAX0714-6519746

Emailinfo@hubeikaixin.com

AddNo.37 Huahu Ave Huahu Street.Huangshi City Hubei

Code435000

web:www.kxdiesteel.com